Abstract In this study, the leaching performance of boron compounds from Oriental beech (Fagus orientalis L.) wood coated with polyurethane/polyurea (PUU) hybrid resin and epoxy resin (EPR) was investigated. Leaching of boron test and SEM (Scanning Electron Microscopy) analyzes were applied to the prepared test specimens. According to the leaching of boron test results, specimens coated with polyurethane/polyurea (PUU) hybrid resin gave the most positive result against boron leaching. It was found that boric acid (BA) impregnated and epoxy resin (EPR) coated Oriental beech wood showed a smoother surface than other treatment groups.

Abstract This study was designed to investigate physical properties such as color changes after weathering and water absorption (WA) levels, and combustion performance of borates-impregnated and LG-coated Oriental beech wood. Results showed that borates impregnated and LG-coated Oriental beech wood showed positive lightness stability after weathering. The best color stabilization was obtained with LG-coated Oriental beech. Except for the 1 h WA period, LG did not show a water repellent effect after the water absorption test. Borates impregnation before LG-coating caused to decrease in weight loss of Oriental beech after the combustion test. Moreover, the lowest weight losses were obtained in borate impregnated Oriental beech wood.